生漆不仅作为优良涂料，还可以热压加工成型。胡炳环，林金火等采用四氯化锡

生漆不仅作为优良涂料，还可以热压加工成型。
胡炳环，林金火等采用四氯化锡和四氯化硅与漆酚反应制备出漆酚硅锡树脂，具有比生漆更好的热稳定性，热失重50％是对应的稳定为556.2℃，模量E’在98.6MPa 以上，并且还具有良好的耐化学介质、腐蚀性能，树脂可以进行热压加工成型，是性能优良的高分子材料。

결과 (영어) 1:

Lacquer, not only as an excellent paint, you can hot-press molding.Hu Bing-Huan, Lin Jinhuo, used four chloride Tin and four chloride silicon and paint phenol reaction preparation out paint phenol Silicon Tin resin, has than lacquer better of hot stability, hot weightlessness 50% is corresponds to of stable for 556.2 ℃, die volume E' in 98.6MPa above, and also has good of resistance chemical media, and corrosion performance, resin can for hot processing forming, is performance excellent of polymer material.

결과 (영어) 2:

Lacquer paint not only as good, but also hot molding process.
HU Bing ring, forest fire and other gold using tin tetrachloride and silicon tetrachloride reaction with urushiol urushiol prepared tin silicon resin, has better thermal stability than lacquer, TG 50% of corresponding steady 556.2 ℃, modulus E 'in the above 98.6MPa, and also has good chemical resistance, corrosion resistance, hot pressing the resin can be molded, the polymer material is excellent performance.

결과 (영어) 3:

Not only as an excellent lacquer coating, can also be hot forming.
Hu binghuan; Lin Jinhuo etc. using stannic chloride and four chlorinated silicon and urushiol reaction of Urushiol silicon tin resin prepared, with than paint better thermal stability and thermal weight loss of 50% is 55.62 DEG C corresponds to the stable and modulus E 'in more than 98.6MPa, and also has good chemical medium resistance, corrosion resistance, resin can hot pressing molding, polymer materials with excellent properties.